A two pack high build polyamide cured epoxy coating and finish, pigmented with micaceous iron
oxide. Suitable as a high build midcoat or finish in systems for steel substrates.

Primer system- primapox mio

Properties and Areas of Use

– Tough hard wearing film
-Good chemical resistance
– Excellent anticorrosive performance in industrial and marine environments
– Cures at low temperatures

Primer system- primapox mio  Technical Coating Data @ 25 °C for mixed material:

Finish                                                                                   Flat

Color Range                                                                       Grey or red

Solids Volume                                                                   65 ± 2%

Dry Film Thickness Range                                            100-200 µm

Theoretical Spreading Rate                                          6.5 m² / L @ 100 microns DFT
(loss factors will apply in practice)
Surface Dry                                                                       2 hours

Recoat Interval                                                                  8 hours minimum
10 days Maximum.
Complete Cure                                                                    7 days
Pot Life                                                                                4 hours
Flash Point                                                                         27°C
Shelf Life                                                                             12 months (stored in a cool dry place)
Mixing Ratio by Weight                                                    8 Base component
1 Activator Component
VOC                                                                                      399 g/l

Film Thickness and Spreading Rate:     

                                                                            Minimum                              Maximum                             Typical
Film thickness, dry (µm)                                         100                                         200                                       150
Film Thickness, wet(µm)                                         154                                         308                                        231
Theoretical Spreading Rate (m2/L)                       6.5                                          3.25                                       4.3

Suitable Surfaces

– Steel and non ferrous metals properly prepared and blast cleaned to ISO-Sa2½
– Concrete free of contamination, dust and efflorescence, and properly prepared

Bare Steel:

Cleanliness: Blast – cleaning to Sa2 1/2 (ISO-8501-1:2007). Power tool cleaning to min. St2 (ISO 8501-1:2007) may be acceptable, subject to exposure conditions.

Shopprimed Steel:

Clean, dry and undamaged approved shopprimer

Coated Surfaces:

Clean, dry and undamaged compatible primer .

Other Surfaces:

For aluminum substrates, thorough washing and sweeping with a nonmetallic blast medium is required.

Application Conditions

Substrate temperature should be 10°C or above for applicaƟon and during cure and a minimum of 3°C above the dew point. Adequate dry air ventilation is recommended for optimum drying.

Application Information

Thinning should only take place after the two components have been thoroughly mixed.

Brush and Roller

Thin if required with 0-5% Paint Thinner Colorama TH907EP.

Conventional Air Spraying

– Thin with 5-25% Paint Thinner Colorama TH907EP, as required.
– Tip size – 2.0 mm
– Tip pressure – 60 psi (0.4Mpa) approximately

Airless Spraying

– Thin with 0-20% Paint Thinner Colorama TH907EP, as required
– Tip size – 0.58-.79 mm approximately
– Tip pressure – 2100 psi (15Mpa) approximately

Cleaning Thinner

Equipment should be cleaned immediately after use with Paint Thinner Colorama TH907EP.

Drying time:

Drying times are affected by air ventilation, temperature, film thickness and number of coats.
Substrate Temp.                                             10° C                          25° C                         40° C
Surface Dry                                                       4 h                              2 h                               1 h
Through Dry                                                     10 h                            6 h                                4 h
Dry to recoat, minimum                                 12 h                           10 h                               6 h
The given data serve as guideline only. The actual drying time differs according to film thickness,
ventilation, humidity and underlying paint system.


Primer system- primapox mio Keep the containers in a dry, cool, well ventilated space and away from source of heat and ignition. Containers
must be kept tightly closed.

Paint System:

PRIMAPOX Zinc                                  2K 1 x 75 µ
PRIMAPOX MIO                                 1 x 150 µ
URELUX                                                1 x 50 µ


Handle with care. Stir well before use.
Packing Size:                      5 L & 18 L

Summary Safety Information

 Avoid inhalation of spray mist and skin contact by the use of masks, gloves and other
personal protection. Eyes should be cautiously washed with water or proprietary wash, and
medical attention obtained. Skin should be thoroughly washed using a cleanser and soap and
– Product is flammable
– No sparks or flames
– No smoking