Selection & Specification Data
Generic Type Cycloaliphatic Amine Epoxy Acrylate. Highly flexible and
Description non-skid epoxy coating based on high quality epoxy acrylate
resin which combines between adhesion and durability of
epoxies with flexibility common to acrylics, designed to be
used for steel and concrete floors as non-skid coating with
high flexibility to resist cracks and skid in case of high surface
expansion or shrinkage.
Excellent chemical resistance.
Excellent skid, cracks and abrasion resistance.
VOC compliant to current AIM regulations.
Excellent water proofing properties.
Flexible with elongaƟon up to 250%.
Color As per shade card.
Dry Film Thickness 2000-4000 microns per coat.
Solid Volume 99% ± 1%.
Theoretical coverage 0.5 m²/L @ 2000 microns.
VOC Value s 0 g/L.
Dry Temperature Resistance 140ºC (DiscoloraƟon and loss of gloss is observed above 95ºC.
Substrate & Surface Preparation
General Surfaces must be clean and dry. Employ adequate methods to remove
dirt, dust, oil and all other contaminants that could interfere with
adhesion of the coating.
Steel Steel blast cleaned to ISO-Sa2½ and then primed with flexible epoxy
primer or other suitable epoxy primer.
Galvanized Steel Primed with suitable etching primer.
Concrete Concrete must be shoot blasted and repair cracks with a suitable sealant and then primed with a proper epoxy sealer.
Listed below are general equipment guidelines for the application of this product. Job site conditions may require modifications to these guidelines to achieve the desired results. General Guidelines:
Conventional Spray Pressure pot equipped with dual regulators, 3/8” I.D. minimum material hose, .070” I.D. fluid Ɵp and appropriate air cap.
Airless Spray Pump Ratio: 30:1 (min.)
GPM Output: 3.0 (min.)
Material Hose: 3/8” I.D. (min.)
Tip Size: .017”-.021”
Output PSI: 2100-2300
Filter Size: 60 mesh
Brush & Roller (Genaral) Multiple coats may be required to obtain desired appearance,
recommended dry film thickness and adequate hiding. Avoid
excessive re-brushing or rerolling. For best results, tie-in
within 10 minutes at 24°C.
Brush Use a medium bristle brush.
Roller Use a short-nap synthetic roller cover with phenolic core.
Mixing & Thinning
Mixing Power mix separately, then combine and power mix.
DO NOT MIX PARTIAL KITS.
Ratio (by Weight) One part component (B) to be added to five parts of
component (A) A:B 5:1
Thinning EPOFLEX TEX is a solvent free coating and no thinning is required.
Pot Life (25ºC) 45 min.
Cleaning Equipments Colorama Thinner No. 907EP
Condition Material Surface Ambient Humidity
Normal 15º-35ºC 15º-35ºC 15º-35ºC 0-85 %
Minimum 10ºC 10ºC 10ºC 0 %
Maximum 37ºC 55ºC 45ºC 85 %
This product simply requires the substrate temperature to be above the dew point. Condensation due to substrate temperatures below the dew point can cause flash rusting on prepared steel and interfere with proper adhesion to the substrate. Special
application techniques may be required above or below normal application conditions
Surface Temperature % 50% R.H. Dry to Recoat Complete Cure
10ºC 36 hours 10 days
15ºC 24 hours 7 days
25ºC 16 hours 5 days
35ºC 8 hours 4 days
Higher film thickness, insufficient ventilation or cooler temperatures will require longer cure times. Excessive humidity or condensation on the surface during curing can interfere with the cure, can cause discoloration and may result in a surface haze. Any haze or blush must be removed by water washing before recoating. During high humidity conditions, it
is recommended that the application be done while temperatures are increasing. Maximum recoat/topcoat times are 30 days for epoxies and 90 days for polyurethanes at 75°F (24°C). If the maximum recoat times have been exceeded, the surface must be abraded by sweep blasƟng or sanding prior to the application of addiƟonal coats. 890 LT applied
below 50°F (10°C) may temporarily soŌen as temperatures rise to 60°F (16°C). This is a normal condition and will not affect performance.
Packaging, Handling & Storage
Packaging 5 L and 18 L
Flash Point(Setaflash) > 100ºC
Storage Temp. & Humidity 10º-40ºC
Shelf Life 24 months @ 25ºC
Shelf life : (actual stated shelf life) when kept at recommended Storage conditions and in
original unopened containers.