SF Epoxy Putty 2K

SF Epoxy Putty 2K – Floor Coatings – Putty A solvent free two pack polyamine cured epoxy putty used in the maintenance of steel and concrete surfaces.

Product description

SF Epoxy Putty 2K – Floor Coatings – Putty A solvent free two pack polyamine cured epoxy putty used in the maintenance of steel and concrete surfaces.

Properties and Areas of Use

– Tough, hard wearing and elastic film
– Excellent water and corrosion resistance in industrial and marine exposure
– Excellent filling with no shrinkage.

Technical Coating Data @ 25 °C for mixed material

Finish                                                                                    Flat
Color Range                                                                         White or Grey
Solids Volume                                                                     100%
Dry Film Thickness Range                                               200-5000 µm
Theoretical Spreading Rate                                              5 m² / L @ 200 microns DFT
(loss factors will apply in practice)
Surface Dry                                                                          1 hrs
Recoat Interval                                                                    12 h
maximum unlimited
Complete Cure                                                                    7 days
Pot Life                                                                                    45 min
Flash Point                                                                             >100°C
Shelf Life                                                                                12 months (stored in a cool dry place)
Mixing Ratio by Weight                                                     3 Base component
1 Activator component
VOC                                                                                         zero
Standability After                                                                  12 h

Film Thickness and Spreading Rate:
                                                                 Minimum                            Maximum                                Typical

Film thickness, dry (µm)                                         200                                          5000                                                3000
Film Thickness, wet(µm)                                         200                                          5000                                                3000
Theoretical Spreading Rate (m2/L)                         5                                               0.2                                                  0.33

Suitable Surfaces

– Steel and nonferrous metals properly prepared and blast cleaned to SIS-Sa 21/2minimum and primed
-Fiberglass, concrete and mineral substrates free of contamination, dust and efflorescence, and properly prepared

Bare Steel:

Cleanliness: Blast – cleaning to Sa2 1/2 (ISO-8501-1:2007). Power tool cleaning to min. St2 (ISO 8501-1:2007) may be acceptable, subject to exposure conditions.

Shop primed Steel:

Clean, dry and undamaged approved shop primer

Coated Surfaces:

Clean, dry and undamaged compatible primer .

Other Surfaces:

For aluminum substrates , thorough washing and sweeping with a nonmetallic blast medium is required.

Application Conditions

Substrate temperature can be 10°C or above for application and during cure and a minimum

of 3°C above the dew point. Adequate dry air ventilation is recommended for optimum drying.

Relative humidity must be below 80% during application. Application Information Component C

(filler) to be added to component A (Resin) slowly using a mechanical agitator at 300 rpm till a uniform

consistency, and then component B (activator) to be added to the

mixture during mechanical sheer and the final mixture should be applied within 45 min.

Application Method

– Using a drawknife or a putty applicator, apply a coat of epoxy putty to fill the area to be maintained.

Cleaning Thinner

Equipment should be cleaned immediately Auer use with Paint Thinner Colorama TH907EP.

Drying time:

Drying times are affected by air ventilation, temperature, film thickness and number of coats.
Substrate Temp.                                                                          10° C                                          25° C                                            40° C
Surface Dry                                                                                     4 h                                            1 h                                               40 min.
Through Dry                                                                                  12 h                                           8 h                                               4 h
Dry to recoat, minimum                                                              16 h                                          12 h                                               8 h
The given data serve as guideline only. The actual drying time differs according to film thickness, ventilation, humidity and underlying paint system.


Keep the containers in a dry, cool, well ventilated space and away from source of heat and ignition. Containers must be kept tightly closed.


Handle with care

Packing Size:

5 L & 18 L

Summary Safety Information

– Avoid inhalation of spray mist and skin contact by the use of masks, gloves and other personal protection. Eyes should be cautiously washed with water or
proprietary wash, and medical attention obtained. Skin should be thoroughly washed using a cleanser and soap and water.
– Product is flammable
– No sparks or flames
-No smoking

SF Epoxy Putty 2K – Floor Coatings – Putty


There are no reviews yet.

Be the first to review “SF Epoxy Putty 2K”

Your email address will not be published. Required fields are marked *

Shopping Cart
Open chat
Scan the code
Can we help you?