A two pack moisture curing inorganic ethyl zinc silicate primer and coating.

Product description

SILPROTECT Anticorrosive A two pack moisture curing inorganic ethyl zinc silicate primer and coating.

Properties and Areas of Use

Excellent anticorrosive properties
Used as a tank lining or as a high performance system primer
Resists splash of strong solvents
Very good impact and abrasion resistance
Temperature range of coated substrate can vary from -50C to +600C
Do not expose to severe acidic or alkaline mediums

Technical Coating Data @ 25 °C for mixed material  

Finish                                                                                            Flat

Color Range                                                                                 Grey

Solids Volume                                                                             65 ± 2%

Dry Film Thickness Range                                                       50-125 µm

Theoretical Spreading Rate                                                    8.67 m² / L @ 75 microns DFT
(loss factors will apply in practice)
Surface Dry                                                                                 30 min.

Recoat Interval                                                                           16 hours minimum
7 days maximum
Complete Cure                                                                            24 hours
Pot Life                                                                                         3 hours
Flash Point                                                                                   12°C
Shelf Life                                                                                      6 months minimum for binder part
12 months minimum for pigment part
Mixing Ratio by Weight                                                            30 Part A (Liquid)
70 Part B (Powder)
VOC                                                                                                326 g/L

Film Thickness and Spreading Rate:   


      Minimum                   Maximum                  Typical
Film thickness, dry (µm)                                             50                                  125                             75
Film Thickness, wet(µm)                                              77                                 192                             115
Theoretical Spreading Rate (m2/L)                           13                                   5.2                            8.67

Suitable Surfaces

Steel and non ferrous metals properly prepared and blast cleaned to ISO-Sa2½

Concrete free of contamination, dust and efflorescence, and properly prepared

Bare Steel:

Cleanliness: Blast – cleaning to Sa2 1/2 (ISO-8501-1:2007). Power tool cleaning to min. St2 (ISO 8501-1:2007) may be acceptable, subject to exposure conditions.

Shopprimed Steel:

Clean, dry and undamaged approved shopprimer

Coated Surfaces:

Clean, dry and undamaged compatible primer .

Other Surfaces:

For aluminum substrates , thorough washing and sweeping with a nonmetallic blast medium is required.

Application Conditions

Substrate temperature should be 10°C or above for application and during cure and a minimum of
3°C above the dew point. Adequate dry air ventilation is recommended for optimum drying.

Application Information

Thinning should only take place after the two components have been thoroughly mixed.

Brush and Roller

Thin if required with 0-5% Paint Thinner Colorama TH933.

Conventional Air Spraying

Thin with 5-25% Paint Thinner Colorama TH933, as required.
Tip size – 2.0 mm
Tip pressure – 60 psi (0.4Mpa) approximately

Airless Spraying

Thin with 0-20% Paint Thinner Colorama TH933, as required
Tip size – 0.58-.79 mm approximately
Tip pressure – 2100 psi (15Mpa) approximately

Cleaning Thinner

Equipment should be cleaned immediately after use with Paint Thinner Colorama TH933.

Drying time:

Drying times are affected by air ventilation, temperature, film thickness and number of coats.
Substrate Temp.                                                            10° C                            25° C                        40° C
Surface Dry                                                                       1 h                             30 min                     15 min
Through Dry                                                                      16                                 8                                  6
Dry to recoat, minimum                                                  24                                16                               12
The given data serve as guideline only. The actual drying time differs according to film thickness,
ventilation, humidity and underlying paint system.

SILPROTECT Anticorrosive
Typical paint system:

SILPROTECT                          1 x 75 µ
PRIMAPOX MIO                   1 x 150 µ
URELUX                                 1 x 50 µ


Keep the containers in a dry, cool, well ventilated space and away from source of heat and ignition. Containers must be kept tightly closed.


Handle with care. Stir well before use.
Packing Size:                               18 L

 Summary Safety Information

– Avoid inhalation of spray mist and skin contact by the use of masks, gloves and other
personal protection. Eyes should be cautiously washed with water or proprietary wash, and
medical attention obtained. Skin should be thoroughly washed using a cleanser and soap and
– Product is flammable
– No sparks or flames
– No smoking

SILPROTECT Anticorrosive


There are no reviews yet.

Be the first to review “SILPROTECT”

Your email address will not be published. Required fields are marked *

Shopping Cart
Open chat
Scan the code
Can we help you?